3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8854 filled with 11 percent carbon fibre and graphite, free flow compound
If transport or storage temperatures are too high the material can agglomerate in its container. In such cases, it is advisable to store the material for 48 hours at below 23c and then to sieve it (mesh size 4mm) before filling the mold. To achieve optimum properties, compression molding should be carried out within a temperature range of 23c to 26c and a humidity range of 45 to 55 percent and a pressure of 55 MPa. The sintering temperature should be in the range of 365c.